Environmental effects on the strength and impact damage resistance of alumina based oxide/oxide ceramic matrix composites

In this study the effects of high temperature and moisture on the impact damage resistance and mechanical strength of Nextel 610/alumina silicate ceramic matrix composites were experimentally evaluated. Composite laminates were exposed to either a 1050°C isothermal furnace-based environment for 30 consecutive days at 6 h a day, or 95% relative humidity environment for 13 consecutive days at 67°C. Low velocity impact, tensile and short beam strength tests were performed on both ambient and environmentally conditioned laminates and damage was characterized using a combination of non-destructive and destructive techniques. High temperature and humidity environmental exposure adversely affected the impact resistance of the composite laminates. For all the environments, planar internal damage area was greater than the back side dent area, which in turn was greater than the impactor side dent area. Evidence of environmental embrittlement through a stiffer tensile response was noted for the high temperature exposed laminates while the short beam strength tests showed greater propensity for interlaminar shear failure in the moisture exposed laminates. Destructive evaluations exposed larger, more pronounced delaminations in the environmentally conditioned laminates in comparison to the ambient ones. External damage metrics of the impactor side dent depth and area directly influenced the post-impact tensile strength of the laminates while no such trend between internal damage area and residual strength could be ascertained.     

巨型水轮发电机剪断销研发与质量控制

为获得设计需要的巨型水轮发电机剪断销的剪切力,得到剪切力波动受控的批量剪断销,通过拉伸试验、冲击试验、硬度试验和剪断销剪切试验等讨论了全尺寸剪断销剪切试验的可行性,分析了剪切试验时正常剪断和非正常剪断的剪断销材料性能差异,探究了剪断销的剪切力质量稳定性控制方法。结果表明:控制剪断销料坯的布氏硬度波动,可实现间接控制剪断销剪切强度的波动;通过试验总结的六步法可达到控制批量剪断销质量和剪切力波动的目的。     

Tuning of shear thickening behavior and elastic strength of polyvinylidene fluoride via doping of ZnO-graphene

ZnO rice like nonarchitects are grafted on the graphene carbon core via a rapid microwave synthesis route. The prepared grafted systems are characterized via XRD, SEM, RAMAN, and XPS to examined the structural and morphological parameters. Zinc oxide grafted graphene sheets (ZnO-G) are further doped in β-phase of polyvinylidene fluoride (PVDF) to prepare the polymer nanocomposites (PNCs) via mixed solvent approach (THF/DMF). β-phase confirmation of PVDF PNCs is done by FTIR studies. It is observed that ZnO-G filler enhances the β-phase content in the PNCs. Non-doped PVDF and PNCs are further studied for rheological behavior under the shear rate of 1–100 s⁻¹. Doping of ZnO-G dopant to the PVDF matrix changes its discontinuous shear thickening (DST) behavior to continues shear thickening behavior (CST). Hydrocluster formation and their interaction with the dopant could be the reason for this striking DST to CST behavioral change. Strain amplitude sweep (10⁻³% -10%) oscillatory test reveals that the PNCs shows extended linear viscoelastic region with high elastic modulus and lower viscous modulus. Effective shear thickening behavior and strong elastic strength of these PNCs present their candidature for various fields including mechanical and soft body armor applications.     

钢管套筒灌浆连接轴向受拉性能模拟试验研究

为研究钢管套筒灌浆连接轴向受拉破坏过程及破坏机理，试验中设计了16组48个钢管套筒灌浆连接试件，试件采用钢板代替圆钢管，并进行静载试验。分析了灌浆料裂缝扩展过程、荷载-相对位移曲线，并对抗剪键高距比、灌浆料厚度、侧向力等因素对破坏过程及承载力的影响进行分析。结果表明：对于不设置抗剪键的套筒灌浆连接试件，斜裂缝随机产生，裂缝分布不均匀；对于设置抗剪键的套筒灌浆连接试件，裂缝首先出现在底部抗剪键位置处，与水平方向夹角约为30°，随后在中部和上部抗剪键位置处分别出现斜裂缝。由于每个抗剪键上荷载分担并不均匀，与抗剪键接触的灌浆料逐渐达到极限压应力，达到极限状态时，承载力全部由抗剪键间的机械咬合力承担，在连接承载力中，可忽略摩擦力和胶结力作用。随着抗剪键高距比h/s增大，各试件初始剪切刚度相差不大，承载力增大，但增幅逐渐减小，建议抗剪键高距比0.06g/s>0.3，同时需要满足灌浆料灌注的施工要求。     

Sensitivity analysis of Johnson-Cook material parameters on adiabatic shear in different directions

ABSTRACT

This study investigates the effects of strain, strain rates, and forming directions (RD-rolling direction, TD-transverse direction, and ND-normal direction) on adiabatic shear, via dynamic impact compression tests using the Split Hopkinson Pressure Bar (SHPB) apparatus. A modified Johnson-Cook (J-C) constitutive model is proposed, which used to analyse the influence of the constitutive parameters on the sensitivity of adiabatic shear, employing a finite element software. The different sensitivities of adiabatic shear under different directions are explained by combining microscopic analysis and results from mechanical responses. The results show that the sensitivity of adiabatic shear can be related to the time of stress collapse in the following trend: ND?>?TD?>?RD; the sensitivities of these constitutive parameters on adiabatic shear are calculated and compared.     

钴/镍复合中间层真空扩散连接钨与钢

以钴粉/镍箔为复合中间层，采用800，900和1 000 ℃等三种连接温度，加压10 MPa并保温120 min的工艺条件，对钨/钢真空扩散连接. 研究了接头的微观组织、成分分布、力学性能及断口特征. 结果表明，连接温度为800 ℃和900 ℃时，钨/中间层界面金属间化合物生成很少，对应接头抗剪强度分别为186 MPa和172 MPa，断口均位于钨母材中近界面的位置，为典型解理断裂形貌；当连接温度升至1 000 ℃时，钨/中间层界面生成厚度小于2 μm的连续金属间化合物层，接头抗剪强度降至115 MPa，断裂也发生在钨母材中近界面的位置，断口大部分区域为沿晶断裂特征.     

粉土界面恒刚度循环剪切试验研究

竖向循环荷载作用下桩土界面的作用机理是研究桩土摩擦疲劳的关键。针对循环荷载作用下桩-粉土界面的剪切性能,使用改进的剪切试验装置在恒刚度条件下进行循环剪切试验,研究循环次数、累积位移和法向刚度对其摩擦疲劳性能、循环后单调剪切性能的影响。试验结果表明,粉土在循环剪切过程中,法向应力和剪应力在初始10个循环内随循环数增加快速衰减,随着循环进行,逐渐趋于稳定;单次循环内在剪切位移方向变化时,土体呈现表现出剪缩-剪胀-剪缩交替现象,总体变形呈现剪缩的趋势;循环荷载作用下,粉土界面的法向应力和剪应力随法向刚度增大衰减速率增大,达到稳定的累积循环位移越小;粉土循环后的单调剪切、法向应力恢复的单调剪切的剪应力比小于首次单调剪切试验值,且法向应力恢复的循环后剪切试验的剪胀程度较小,表明循环剪切过程中界面处粉土颗粒棱角破碎,颗粒变得光滑。在对试验数据分析的基础上,提出了与累积位移、法向刚度和初始应力相关的无量纲累积位移,建立了法向应力和界面摩擦角随累积位移的衰减方程。     

An approach to measure infill matric suction of irregular infilled rock joints under constant normal stiffness shearing

Rock joints infilled with sediments can strongly influence the strength of rock mass. As infilled joints often exist under unsaturated condition, this study investigated the influence of matric suction of infill on the overall joint shear strength. A novel technique that allows direct measurement of matric suction of infill using high capacity tensiometers (HCTs) during direct shear of infilled joints under constant normal stiffness (CNS) is described. The CNS apparatus was modified to accommodate the HCT and the procedure is explained in detail. Joint specimens were simulated by gypsum plaster using three-dimensional (3D) printed surface moulds, and filled with kaolin and sand mixture prepared at different water contents. Shear behaviours of both planar infilled joints and rough joints having joint roughness coefficients (JRCs) of 8–10 and 18–20 with the ratios of infill thickness to asperity height (t/a) equal to 0.5 were investigated. Matric suction shows predominantly unimodal behaviour during shearing of both planar and rough joints, which is closely associated with the variation of unloading rate and volumetric changes of the infill material. As expected, two-peak behaviour was observed for the rough joints and both peaks increased with the increase of infill matric suction. The results suggest that the contribution of matric suction of infill on the joint peak normalised shear stress is relatively independent of the joint roughness.     

潮流能水平轴水轮机在剪切来流下的水动力分析

采用基于计算流体力学方法的全尺度数值模拟计算,建立了适用于潮流能水轮机模拟的剪切来流环境,通过数值计算结果,对潮流能水轮机随时间变化的宏观力和流场特征进行了系统分析,探索水轮机在复杂工况下的水动力特性规律。结果表明,水轮机整个叶轮的总体平均受力在剪切流工况中未受到明显影响; 单个叶片的瞬态轴向力系数和瞬态轴向扭矩系数在旋转周期内出现了明显的周期性变化,且周期性变化幅值随转速增大而增大; 非定常的瞬时轴向扭矩和力的周期性振荡容易引起单个叶片的结构性振动,可能对水轮机的机械结构造成影响。     

基于3D打印技术复制砂浆节理的剪切试验及峰值抗剪强度模型

为进一步研究节理三维形貌特征与节理峰值抗剪强度的关系,首先采用巴西劈裂试验获取了自然劈裂岩石表面,通过三维扫描技术获取了节理面形态的高精度点云,通过逆向建模得到了自然岩石表面的立体模型,结合3D打印技术制作出了与自然岩石表面一致的PLA模具,以3D打印获得的底模通过水泥砂浆浇筑了含有自然结构面形貌的相似节理面试样。PLA模具与复制材料差异较大,复制材料在凝结过程中不易与PLA模具黏结,进而使脱模过程较为方便,不会破坏节理面。同时PLA模具可重复进行相似材料复制工作,具有可重复使用的优点。然后进行了具有5组形貌面的20个水泥砂浆节理面在4种不同法向荷载情况下的结构面剪切试验,得到了结构面剪切位移-荷载曲线。研究了结构面峰值抗剪强度、峰值位移、剪切刚度影响因素。节理经过剪切后形貌面出现不同程度的磨损,其磨损范围与等效高差分布范围基本一致,并且在等效高差为剪断破坏模式且成片的区域磨损较为严重。在新粗糙度指标基础上提出了新的峰值抗剪强度模型,经试验对比显示出新模型的有效性。在新模型基础上提出了一个简化模型。对比发现新模型简化后其计算精度较新模型有所降低但由于所需参数减小计算较为方便,新模型简化结果精度虽然有所下降但是还是比Barton公式精度高。